I-Raw Material Magnesium Hydroxide Fire Retardant ebangeni Lemboni
Ukucaciswa
I-Magnesium Hydrooxide | ||||||||
Uchungechunge lokuhlanzeka okuphezulu | Ibanga lezimboni | Ibanga lezemithi | ||||||
Inkomba | ZH-H2-1 | ZH-H2-2 | ZH-H3-1 | ZH-H5 | ZH-E6A | ZH-E6B | ZH-HUSPL | ZH-HUSPH |
Mg(OH)2 ≥ (%) | 99 | 99 | 99 | 99 | 95-100.5 | 95-100.5 | ||
I-MgO≥ (%) | 60 | 55 | ||||||
Ca ≤ (%) | 0.05 | 0.05 | 0.05 | 0.05 | 2 | 3 | 1.5 | 1.5 |
Ukulahlekelwa ekushiseni≥ (%) | 30 | 30 | 30 | 30 | 30-33 | 30-33 | 30-33 | 30-33 |
I-Acid-insoluble ≤ (%) | 0.1 | 0.1 | 0.1 | 0.1 | ||||
Cl ≤ (%) | 0.6 | 0.6 | 0.6 | 0.6 | 0.05 | 0.05 | ||
Amanzi ≤ (%) | 0.5 | 2 | 2 | |||||
Fe ≤ (%) | 0.05 | 0.05 | 0.05 | 0.05 | 0.5 | |||
SO4≤ (%) | 0.5 | 0.5 | 0.5 | 0.5 | ||||
Ubumhlophe ≥ (%) | 95 | 90 | 90 | |||||
Usawoti Oncibilikayo≤ (%) | 0.5 | 0.5 | ||||||
usayizi D50≤ (um) | 2 | 3 | 4.5 | 40-60 | 3/4.5 | 4.5 | ||
usayizi D100 ≤ (um) | 25 | |||||||
Ukuhola≤ (ppm) | 1.5 | 1.5 | ||||||
Indawo ethile (m2/g) | 20 | 20 | ||||||
Ukuminyana kwenqwaba(g/ml) | ≤0.4 | ≤0.4 | ≤0.4 | ≥0.6 | ≤0.5 | ≤0.5 | ≤0.4 | ≥0.4 |
Izicelo ku-Industrial
1. Ukususwa komthofu nokususwa kombala.
2. Heavy metal adsorbent.
3. Imibala elwa namagciwane.
4. Isithasiselo sikawoyela ukuvimbela ukugqwala nokukhishwa kwesulfurization.
5. I-ejenti engathathi hlangothi ye-asidi equkethe amanzi angcolile.
Ukupakisha Umkhiqizo
Ipakishwe ezikhwameni ezilukiwe ezifakwe ulayini wepulasitiki ezinenethi engu-20/25kg ngayinye.
Mg(OH)2 izicelo
Ifaneleka kakhulu ezidingweni zepulasitiki zokucubungula izinga lokushisa eliphezulu.I-Magnesium hydroxide ingasetshenziswa njenge-flame retardant njenge-polyethylene, i-polypropylene, i-polyvinyl chloride, i-triathoolite, i-polyester engasetshenzisiwe kanye nezinye ipulasitiki nerabha.Ingasetshenziswa futhi njenge-flame retardant yokugqoka.
I-Magnesium hydroxide isetshenziswa njengokwelashwa kwamanzi angcolile, ukuchithwa kwezinsimbi ezinzima, ukwelashwa kwe-seal nokudaya amanzi angcolile, ukwelashwa kwe-arsenic namanzi angcolile, njll.
I-Magnesium hydroxide isetshenziswa njenge-desulfurization yentuthu.
Isevisi kanye nekhwalithi
Umhlabathi wethu omuhle wemvelo I-Magnesium hydroxide isetshenziswa kakhulu njenge-retardant ye-flame in thermoplastic kanye ne-elastomer polymer compounds.Ingasetshenziswa futhi njengengxenye yamapende nama-resin, uphahla lwe-TPO kanye nezicelo zephansi kanye namaphaneli e-Aluminium Composite.